No2 Dong TaunRd Zanan IndustriaL ZONE | ||||||
Solar Surface Absorption Test |
||||||
Test time:2024.04.15(13:20-15:20) Duration of direct sunlight exposure ( 2 hours)Test time:2024.04.16(13:10-14:20)Test Method: ASTM E903-20 SleekTEAK and EVA (foam) Test method:Equal samples were placed on a metallic sheet exposed to direct sunlight for two hours. The surface temperature of each sample was then measured to evaluate thermal performance. Test time:2024.05.06(13.10-14:30)Test Data: | ||||||
Ambient Temperature:35.0℃ | ||||||
- | 1 | 2 | 3 | 4 | 5 | Average Value |
Ground temperature(℃) | 34.2 °C | 34.1 °C | 34.2 °C | 34.1 °C | 34.2 °C | 34.2 °C |
Metallic substrate temperature(℃) | 37.2 °C | 37.1 °C | 37.2 °C | 37.1 °C | 37.2 °C | 37.2 °C |
EVA Grey(℃) | 43.2 °C | 43.1 °C | 43.3 °C | 43.2 °C | 43.4 °C | 43.2 °C |
EVA Brown(℃) | 39.9 °C | 39.8 °C | 40.0 °C | 40.1 °C | 39.9 °C | 39.9 °C |
SleekTEAK Grey(℃) | 39.5 °C | 39.5 °C | 39.6 °C | 39.7 °C | 39.5 °C | 39.6 °C |
SleekTEAK Brown (℃) | 40.2 °C | 40.1 °C | 40.2 °C | 40.1 °C | 40.2 °C | 40.2 °C |
Solar Surface Absorption Test |
||||||
Test method:Equal samples were placed on a metallic sheet exposed to direct sunlight for two hours. The surface temperature of each sample was then measured to evaluate thermal performance. | ||||||
Test Method: ASTM E903-20 SleekTEAK and EVA (foam) Test time:2024.05.07(13.00-14:30) |
||||||
Ambient Temperature:48.0℃ | ||||||
Test Data: | ||||||
- | 1 | 2 | 3 | 4 | 5 | Average Value |
Ground temperature(℃) | 43.4 °C | 43.5 °C | 43.3 °C | 43.4 °C | 43.4 °C | 43.4 °C |
Metalic substrate temperature(℃) | 48.7 °C | 48.9 °C | 48.7 °C | 48.7 °C | 48.9 °C | 48.8 °C |
EVA Grey(℃) | 50.5 °C | 50.4 °C | 50.5 °C | 50.3 °C | 50.2 °C | 50.4 °C |
EVA Brown(℃) | 52.0 °C | 52.1 °C | 52.2 °C | 51.9 °C | 51.9 °C | 52.0 °C |
SleekTEAK Grey (℃) | 50.0 °C | 50.0 °C | 50.1 °C | 50.0 °C | 50.3 °C | 50.1 °C |
SleekTEAK Brown(℃) | 53.4 °C | 53.2 °C | 53.4 °C | 53.5 °C | 53.2 °C | 53.3 °C |
Solar Surface Absorption Test |
||||||
Test method:Equal samples were placed on a metallic sheet exposed to direct sunlight for two hours. The surface temperature of each sample was then measured to evaluate thermal performance. | ||||||
Test Method: ASTM E903-20 SleekTEAK and EVA (foam) | ||||||
Test time:2024.05.16(13.00-14:30) |
||||||
Ambient temperature:43.3℃ | ||||||
Test Data: | ||||||
- | 1 | 2 | 3 | 4 | 5 | Average Value |
Ground Temperature(℃) | 46.3 °C | 46.4 °C | 46.3 °C | 46.3 °C | 46.5 °C | 46.4 °C |
Metallic substrate Temperature(℃) | 46.5 °C | 46.5 °C | 46.6 °C | 46.6 °C | 46.7 °C | 46.6 °C |
EVA Grey(℃) | 51.8 °C | 51.7 °C | 51.6 °C | 51.8 °C | 51.8 °C | 51.7 °C |
EVA Brown(℃) | 51.1 °C | 51.2 °C | 51.0 °C | 51.1 °C | 51.3 °C | 51.1 °C |
SleekTEAK Grey(℃) | 52.0 °C | 52.0 °C | 52.1 °C | 52.2 °C | 52.3 °C | 52.1 °C |
SleekTEAK Brown(℃) | 58.8 °C | 58.7 °C | 58.6 °C | 58.7 °C | 58.6 °C | 58.7 °C |
SleekTEAK Red(℃) | 49.8 °C | 49.9 °C | 49.9 °C | 49.8 °C | 49.7 °C | 49.8 °C |
SleekTEAK Blue(℃) | 53.7 °C | 53.6 °C | 53.7 °C | 53.7 °C | 53.6 °C | 53.7 °C |
SleekTEAK Yellow(℃) | 50.3 °C | 50.4 °C | 50.5 °C | 50.3 °C | 50.4 °C | 50.4 °C |